The effect of peak cladding temperature occurring during interim-dry storage on transport-induced cladding embrittlement

김규태 2020년

논문상세정보
인용/피인용
' The effect of peak cladding temperature occurring during interim-dry storage on transport-induced cladding embrittlement' 의 주제별 논문영향력
논문영향력 선정 방법
논문영향력 요약
주제
  • Cladding hoop stress
  • Offset strain
  • Peak cladding temperature
  • Radial hydride fraction
  • Ring compression tests
동일주제 총논문수 논문피인용 총횟수 주제별 논문영향력의 평균
12 0

0.0%

' The effect of peak cladding temperature occurring during interim-dry storage on transport-induced cladding embrittlement' 의 참고문헌

  • H. Chung [2000]
  • S. Yagnik [2004]
  • 피복관 열화거동에 미치는 수소화물 영향 평가
    김현길 [2010]
  • Understanding hydride- and hydrogen-related processes in highburnup cladding in spent-fuel storage and accident situations
    H. Chung [2004]
  • The effect of texture variation on delayed hydride cracking behavior of Zre2. 5%Nb plate
    S. Kim [1999]
  • Terminal cool-down temperature-dependent hydride reorientation in ZreNb Alloy claddings under dry storage conditions
    S. Min [2014]
  • Stress-reorientation of hydrides and hydride embrittlement of Zre2. 5 wt% Nb pressure tube alloy
    R. Singh [2004]
  • Simulation of hydrogen embrittlement in zirconium alloys under stress and temperature gradients
    A. Varias [2000]
  • Occurrence of ductile hydrides in Zircaloy-2
    G. Parry [1964]
  • Integrity criteria of spent fuel for dry storage in Japan
    K. Kimura [2010]
  • Influence of temperature on threshold stress for reorientation of hydrides and residual stress variation across thickness of Zre2. 5Nb alloy pressure tube
    R. Singh [2006]
  • In situ study of hydride precipitation kinetics and re-orientation in Zircaloy using synchrotron radiation
    K. Colas [2010]
  • Hydrogen Solubility and Microstructural Changes in Zircaloy-4 Due to Neutron Irradiation
  • Hydride-induced degradation of hoop ductility in textured zirconium-alloy tubes : a theoretical analysis
    W. Qin [2012]
  • Hydride embrittlement in Zircaloy-4plate: Part II. interaction between the tensile stress and the hydride morphology
    J. Bai [1994]
  • Examination of Spent PWR Fuel Rods after 15 Years in Dry Storage
    ANL [2003]
  • Effects of hydrogen content and temperature on fracture toughness of Zircaloy-4
  • Effects of hydride morphology on the embrittlement of Zircaloy-4 cladding
    J. Kim [2015]
  • Effect of radial hydrides on the axial and hoop mechanical properties of Zircaloy-4 cladding
    H. Chu [2007]
  • Ductile-to-brittle transition temperature for high-burnup cladding alloys exposed to simulated drying-storage conditions
  • Cooling rate-and hydrogen content-dependent hydride reorientation and mechanical property degradation of ZreNb alloy claddings
    S. Min [2013]
  • Control of hydride orientation in Zircaloy
  • Cladding considerations for the transportation and storage of spent fuel
    USNRC [2003]
  • An allowable cladding peak temperature for spent nuclear fuels in interim dry storage
    H. Cha [2018]
  • A hydrogen uptake micro-mechanism for Zr alloys
    B. Cox [1999]