Crack growth and cracking behavior of Alloy 600/182 and Alloy 690/152 welds in simulated PWR primary water

임연수 김동진 김성우 김홍표 2019년

논문상세정보
인용/피인용
' Crack growth and cracking behavior of Alloy 600/182 and Alloy 690/152 welds in simulated PWR primary water' 의 주제별 논문영향력
논문영향력 선정 방법
논문영향력 요약
주제
  • Alloys 600/182
  • Alloys 690/152
  • crack growth rate
  • crackpropagation
  • pwscc
  • welding
동일주제 총논문수 논문피인용 총횟수 주제별 논문영향력의 평균
127 0

0.0%

' Crack growth and cracking behavior of Alloy 600/182 and Alloy 690/152 welds in simulated PWR primary water' 의 참고문헌

  • Toward the multiscale nature of stress corrosion cracking
  • The stress corrosion cracking behavior of Alloys 690 and 152 weld in a PWR environment
  • Study on grain boundary character along intergranular stress corrosion crack paths in austenitic alloys
  • SCC of Alloy 152/52/52i weld metals in PWR primary water
  • Role of Grain Boundary Carbides in Cracking Behavior of Ni Base Alloys
    황성식 [2013]
  • Observations and implications of intergranular stress corrosion crack growth of Alloy 152 weld metals in simulated PWR primary water
  • Microstructural characterization of primary water stress-corrosion cracks in Alloy 182 welds from PWR components and laboratory tests
    L.E. Thomas [2009]
  • Microstructural characterization of intergranular stress corrosion cracking of Alloy 600 in PWR primary water environment
    Y. S. Lim [2013]
  • Microscopic examination of an Alloy 600/182 weld
    Y. S. Lim [2009]
  • Measurement of the nickel/nickel oxide transition in Ni-Cr-Fe alloys and updated data and correlations to quantify the effect of aqueous hydrogen on primary water SCC
  • Linking grain boundary micro-structure to stress corrosion cracking of cold-rolled Alloy 690in pressurized water reactor primary water
  • Intergranular oxidation of Nibased Alloy 690 in a simulated PWR primary water environment
    Y. S. Lim [2016]
  • Intergranular environmentally assisted cracking of Alloy 182 weld metal in simulated normal water chemistry of boiling water reactor
    Q. Peng [2007]
  • Influence of oxide films on primary water stress corrosion cracking initiation of alloy 600
    J. Panter [2006]
  • High voltage electron microscopy observations of microdeformation in Alloy 600 tubing
  • Effect of deformation temperature, orientation and carbides on SCC of Alloy 690
  • Development of crack growth rate disposition curves for primary water stress corrosion cracking (PWSCC) of Alloy 82, 182, and 132 weldments
    G.A. White [2005]
  • Degradation of grain boundary strength by oxidation in alloy 600
    K. Fujii [2011]
  • Cracking of Alloy 600 nozzles and welds in PWRs: review of cracking events and repair service experience
    W. Bamford [2005]
  • Crack growth response of Alloy 690 in simulated PWR primary water
  • Crack growth rates for evaluating PWSCC of thick-wall Alloy 600 material
    G.A. White [2003]
  • Crack growth rate measurements in Alloy 182 in PWR primary water at low stress intensity
    A. Jenssen [2015]
  • Behavior of grain boundary chemistry and precipitates upon thermal treatment of controlled purity Alloy 690
  • ASTM-E112-13, Standard test methods for determining average grain size
  • ASTM E647-15, Standard Test Method for Measurement of Fatigue Crack Growth Rates
  • A review of Alloy 600 cracking in operating nuclear plants:historical experience and future trends
    W. Bamford [2003]