Effect of strain hardening on burst pressure of axial cracked U-bend steam generator tubes

김지석 2020년

논문상세정보
인용/피인용
' Effect of strain hardening on burst pressure of axial cracked U-bend steam generator tubes' 의 주제별 논문영향력
논문영향력 선정 방법
논문영향력 요약
주제
  • Finite element damage analysis
  • Strain-hardening
  • U-bend steam generator tubes
  • burstpressure
동일주제 총논문수 논문피인용 총횟수 주제별 논문영향력의 평균
26 0

0.0%

' Effect of strain hardening on burst pressure of axial cracked U-bend steam generator tubes' 의 참고문헌

  • [51] Aptech Engineering Services, "AES 980333327-1Q-1: An Updated Probabilistic Operational Assessment for SONGS Unit 2, Second Mid- Cycle Operating Period," Aptech Engineering Services, Sunnyvale, CA, USA, 1998.
  • [50] Aptech Engineering Services, "AES 96052749-1-1: Analysis of ODSCC/IGA at Tubesheet and Tube Support Locations at St. Lucie, Unit 1," Aptech Engineering Services, Sunnyvale, CA, USA, 1996.
  • [49] B. Cochet and B. Flesch, "Crack Stability Criteria in Steam Generator Tubes," in 9th SMIRT Conference, Lausanne, Switzerland, 1987.
  • [47] Dassault Systems Simulia Corp., "ABAQUS Version 6.13. User¡¯s manual.," Dassault Systems Simulia Corp., RI, USA, 2013
  • [46] B. Flesch and B. Cochet, "Application of the Leak-Before-Break Concept to Steam Generator Tubes," in 10th SMIRT Conference, Anaheim, CA, USA, 1989.
  • [43] G. R. Jonson, and W. H. Cook, "Fracture characteristics of three metals subjected to various strains, strain rates, temperatures and pressures", Eng Fract Mech, vol. 21, no. 1, pp. 31-48, 1985.
  • [42] J. W. B. D. K. Hancock, "On the role of strain and stress state in ductile failure," J Mech Phys Solids, vol. 31, pp. 1-24, 1983.
  • [3] B. Flesch and B. Cochet, "Leak-Before-Break in Steam Generator Tubes," International Journal of Pressure Vessels and Piping, vol. 43, pp. 165-179, 1990.
  • [34] J. R. Rice and D. M. Tracey, "On the ductile enlargement of voids in triaxial stress fields," J Mech Phys Solids, vol. 17, pp. 201-217, 1969.
  • [33] F. A. McClintock, "A criterion for ductile fracture by the growth of holes," J Appl Mech, vol. 35, pp. 363-371, 1968.
  • [29] A. L. Gurson, "Continuum theory of ductile rupture by void nucleation and growth: part I-yield criteria and flow rules for porous ductile media," J Eng Mater Technol., vol. 99, pp. 2-15, 1977.
  • [28] B. Cochet, "Steam Generator Tube Integrity," Electric Power Research Institute and Framatome, Palo Alto, CA. (USA) and Paris (France), 1991.
  • [18] T.J. McGinty, "Crack-like indication in the u-bend region of a thermally treated alloy 600 steam generator tube", NRC information notice 2010- 21.
  • [17] J. Allan, S. Kaufmann, E. Murphy, J. Strosnider, M. Gamborini, D. Lu, T. Sullivan, T. Pitterle, T. Esselman, A. Neff, J. Mark, J. Parry, J. Baumstark, D. Mcadam, D. Adanonis, and G. Henry, "Official Transcript of Proceedings United States of America Nuclear Regulatory Commission: NRC and Consolidated Edison Technical Meeting Regarding IP2 Steam Generator". U.S. Nuclear Regulatory Commission, Washington, DC.
  • Validation of Failure and Leak-Rate Correlations for Stress Corrosion Cracks in Steam Generator Tubes
    [2002]
  • Steam Generator Tube Failures . Idaho Falls ( ID ) : Idaho National Engineering Lab , Div . of Safety Programs
    Report No . NUREG/CR-6365 , INEL- 95/0383 [1996]
  • Steam Generator Management Program : Steam Generator Degradation Specific Management Flaw Handbook , Revision 2 , Cranberry Township ( PA ) : Westinghouse Electric Company
    Report No . 3002005426 . [2015]
  • Status review of initiation of environmentally assisted cracking and short crack growth
    [2005]
  • Standard Test Methods for Tension Testing of Metallic Materials
    [2015]
  • Results From Pressure and Leak-Rate Testing of Laboratory-Degraded Steam Generator Tubes
    [2002]
  • Residual Stresses in Bent Tubes for Nuclear Steam Generators
    vol . 32 , no . 9 , pp . 357-364 , [1976]
  • Repair and replacement applicationsCenter : stressCorrosionCracking inClosedCooling water systems
    [2006]
  • P. Hernalsteen and D. Dobbeni , Belgian Approach to Steam Generator Tube Plugging for Primary Water Stress Corrosion Cracking
    [1990]
  • On the applicability of local approaches for the determination of the failure behavior of ductile steels
    vol . 114 , pp . 214-220 , [1993]
  • Numerical simulation of rotating bending process for U-tubes in heat exchangers ,
    vol . 32 , no . 10 , pp . 809-819 [2009]
  • Numerical prediction of maximum load-carrying capacity of cracked alloy 690TT steam generator tubes
    vol . 138 , no . 4 , p. 041601 [2016]
  • Numerical Validation of Burst Pressure Estimation Equations for Steam Generator Tubes with Multiple Axial Surface Cracks
    vol . 51 , pp . 579-587 [2019]
  • Ligament rupture and unstable burst behaviors of axial flaws in steam generator U-bends
    vol . 293 pp . 228 ? 237 [2015]
  • Indian point 2 steam generator tube failure lessons-learned report . In : TAC No . MA9163 . U.S. Nuclear Regulatory Commission
  • Failure behavior of multiple-axial part-through-wall flaws in alloy 690TT steam generator tubes
    vol . 138 , no . 2 , p. 021406 [2015]
  • Failure Behavior of Internally Pressurized Flawed and Unflawed Steam Generator Tubing at High Temperatures - Experiments and Comparison With Model Predictions
    [1998]
  • Experimental and Numerical Study on the Burst Pressure of Steam Generator Tubes with L- and U- Type Through-Wall Combination Cracks
    vol . 27 , no . 8 , pp . 2299-2304 [2013]
  • Evaluation of the Burst Characteristics for Axial Notches on SG Tubings
    vol . 232 , no . 2 , pp . 139-143 [2004]
  • Evaluation of tensile properties of alloy 690TT steam generator tube at room temperature and 343¡É
    vol . 38 , no . 6 , pp . 655-662 [2014]
  • Effect of Pressurization Rate on Degraded Steam Generator Tubing Burst Pressure : Revision 1
    [2001]
  • Ductile tearing simulation of Battelle pipe test using simplified stressmodified fracture strain concept , Fatigue and Fracture of Engineering 128 Materials and Structures
    vol . 39 , no . 11 , pp . 1391-1406 [2016]
  • Ductile fracture simulation of a pipe of steam generator in PWR. , in The ASME 2013 Pressure Vessels and Piping Conference
    [2013]
  • Ductile fracture models and their potential in local approach of fracture
    vol . 105 , pp . 97-111 [1987]
  • Development and Justification of New plugging Criteria Applicable to the Cracking Phenomena in the Tubing of Steam Generator , BELGATOM
    [1989]
  • Determination of equivalent single crack based on coalescence criterion of collinear axial cracks
    vol . 205 , pp . 1-11 [2001]
  • Determination of Global Failure Pressure for Tubes with Two Parallel Cracks , Fatigue Fract
    vol . 29 , no . 8 , pp . 623-631 [2006]
  • Determination of Failure Pressure for Tubes with Two NonAligned Through-Wall Cracks
    vol . 144 , no . 2 , pp . 91-101 [2007]
  • Damage modeling of the load-bearing capacity of damaged steam generator tubes in nuclear power plants
    [2013]
  • Comparison of numerical predictions with experimental burst pressures of tubes with multiple surface cracks
    vol . 201 pp . 176-195 [2018]
  • C. Vulyak and W. J. Shack , Steam Generator Tube Integrity Issues : Pressurization Rate Effect , Failure Maps , Leak Rate Correlation Models , and Leak Rates in Restricted Areas
    [2009]
  • Burst pressure tests of axial part-through-wall steam generator tubes
    vol . 10 , no . 1 , pp . 56-63 [2014]
  • Burst pressure estimation equations for steam generator tubes with multiple axial surface cracks
    vol . 158 , pp . 59-68 [2017]
  • Application of engineering ductile tearing simulation method to CRIEPI pipe test
    vol . 153 , pp . 128-142 [2016]
  • A numerical method to simulate ductile failure of tensile plates with interacting through-wall cracks ,
    vol . 34 , pp . 215-226 [2011]
  • A finite element ductile failure simulation method using stress-modified fracture strain model
    vol . 78 , no . 1 , pp . 124-137 [2011]
  • 3D-analysis of localization failure in a ductile material containing two size-scales of spherical particles
    vol . 31 , pp . 421-436 [1988]